Highly structured TiO2/In(OH)xSy/PbS/PEDOT:PSS to be used in photovoltaic applications

Abstract

A new highly structured system based on TiO2/In(OH)xSy/PbS/PEDOT:PSS/Au has been developed for photovoltaic applications. In this device, TiO2, In(OH)xSy, PbS and PEDOT:PSS serve as electron conductor, buffer layer, absorber and hole conductor, respectively. Both buffer and absorber layers have been prepared by chemical bath deposition. For annealed In(OH)xSy, an optical band gap of 2.2 eV has been obtained and for PbS the bulk value is widened to about 0.85 eV due to the presence of oxide in the film composition. At present stage, solar cells with such configuration have reached up to about 1% efficiency with Jsc= 8 mA/cm2 and Voc= 0.3 V. To cite this article: R. Bayón et al., C. R. Chimie 9 (2006).RésuméUne nouvelle cellule photovoltaïque fondé sur le système ultra-structuré TiO2/In(OH)xSy/PbS/PEDOT:PSS/Au a été développée. Dans ce dispositif TiO2, In(OH)xSy, PbS et PEDOT:PSS servent de conducteur d'électrons, couche tampon, absorbeur et conducteur de trous respectivement. La couche tampon ainsi que celle d'absorbeur ont été préparées par dépôt chimique en solution. Pour les couches de In(OH)xSy recuites, une énergie de gap de 2,2 eV a été obtenue et, pour celle de PbS, la valeur correspondant au matériau massif a atteint 0,85 eV, en raison de la présence d'oxyde dans la composition de la couche. À présent, les cellules photovoltaïques de cette configuration ont atteint presque 1% de rendement de conversion (Jsc= 8 mA/cm2 et Voc= 0,3 V). Pour citer cet article : R. Bayón et al., C. R. Chimie 9 (2006).